Depth-resolved residual stress analysis with conical slits for highenergy X-rays

Abstract

A conical slit cell for depth-resolved diffraction of high-energy X-rays was tested at the high-energy materials science beamline HEMS at PETRA III and used for the analysis of residual stresses in a laser beam welded steel overlap joint. With a conical slit width of 20 µm and beam cross-sections below 100 µm, depth resolutions well below 1 mm were achieved. The residual stress distributions obtained from the steel joint were in very good agreement with previous results from neutron diffraction measurements, although they were still noisier because of inferior grain statistics.