Shape-memory properties and degradation behavior of multifunctional electro-spun scaffolds

Abstract

Multifunctional polymer-based biomaterials, which combine degradability and shape-memory capability, are promising candidate materials for the realization of active self-anchoring implants. In this work we explored the shape-memory capability as well as the hydrolytic and enzymatic in vitro degradation behavior of electro-spun scaffolds prepared from a multiblock copolymer, containing hydrolytically degradable poly(p-dioxanone) (PPDO) and poly(e-caprolactone) (PCL) segments, which we have named PDC.?Electro-spun PDC scaffolds with an average deposit thickness of 80 ± 20 µm and a porosity in the range from 70% to 80% were prepared, where the single fiber diameter was around 3 µm. Excellent shape-memory properties were achieved with high recovery rate (Rr) values in the range of Rr = 92% to 98% and a recovery stress of smax = 4.6 MPa to 5.0 MPa. The switching temperature (Tsw) and the characteristic temperature obtained under constant strain recovery conditions (Ts,max) were found in the range from 32°C to 35°C, which was close to the melting temperature (Tm,PCL) associated to the poly(e-caprolactone) domains. ?A linear mass loss was observed in both hydrolytic and enzymatic degradation experiments. The mass loss was substantially accelerated, in enzymatic degradation when Pseudomonas cepacia lipase was added, which was reported to accelerate the degradation of PCL. During hydrolytic degradation a continuous decrease in elongation at break (eB) from eB = 800% to 15% was observed in a time period of 92 days, while in enzymatic degradation experiments a complete mechanical failure was obtained after 4 days.