@misc{yang_microstructure_mechanical_2023, author={Yang, L., Huang, Y., Hou. Z., Xiao, L., Xu, Y., Dong, X., Li, F., Kurz, G., Sun, B., Li, Z., Hort, N.}, title={Microstructure, mechanical properties and fracture behaviors of large-scale sand-cast Mg-3Y-2Gd-1Nd-0.4Zr alloy}, year={2023}, howpublished = {journal article}, doi = {https://doi.org/10.1016/j.jma.2021.08.010}, abstract = {In order to improve the ductility of commercial WE43 alloy and reduce its cost, a Mg-3Y-2Gd-1Nd-0.4Zr alloy with a low amount of rare earths was developed and prepared by sand casting with a differential pressure casting system. Its microstructure, mechanical properties and fracture behaviors in the as-cast, solution-treated and as-aged states were evaluated. It is found that the aged alloy exhibited excellent comprehensive mechanical properties owing to the fine dense plate-shaped β' precipitates formed on prismatic habits during aging at 200 °C for 192 hrs after solution-treated at 500 °C for 24 hrs. Its ultimate tensile strength, yield strength, and elongation at ambient temperature reach to 319 ± 10 MPa, 202 ± 2 MPa and 8.7 ± 0.3% as well as 230 ± 4 MPa, 155 ± 1 MPa and 16.0 ± 0.5% at 250 °C. The fracture mode of as-aged alloy was transferred from cleavage at room temperature to quasi-cleavage and ductile fracture at the test temperature 300 °C. The properties of large-scale components fabricated using the developed Mg-3Y-2Gd-1Nd-0.4Zr alloy are better than those of commercial WE43 alloy, suggesting that the new developed alloy is a good candidate to fabricate the large complex thin-walled components.}, note = {Online available at: \url{https://doi.org/10.1016/j.jma.2021.08.010} (DOI). Yang, L.; Huang, Y.; Hou. Z.; Xiao, L.; Xu, Y.; Dong, X.; Li, F.; Kurz, G.; Sun, B.; Li, Z.; Hort, N.: Microstructure, mechanical properties and fracture behaviors of large-scale sand-cast Mg-3Y-2Gd-1Nd-0.4Zr alloy. Journal of Magnesium and Alloys. 2023. vol. 11, no. 8, 2763-2775. DOI: 10.1016/j.jma.2021.08.010}}