@misc{callegari_insitu_synchrotron_2020, 
author={Callegari, B., Oliveira, J., Aristizabal, K., Coelho, R., Brito, P., Wu, L., Schell, N., Soldera, F., Mücklich, F., Pinto, H.},
title={In-situ synchrotron radiation study of the aging response of Ti-6Al-4V alloy with different starting microstructures},
year={2020},
howpublished = {journal article},
doi = {https://doi.org/10.1016/j.matchar.2020.110400},
abstract = {The aging behavior of a Ti-6Al-4V alloy with different starting microstructures was evaluated by means of synchrotron X-ray diffraction, scanning-transmission electron microscopy and micro-hardness measurements. Initial microstructures were produced by thermal and thermomechanical treatments and comprised different morphologies of α phase (martensitic, lamellar, bimodal and globular), as well as the presence or absence of the β phase. Results show that one or more of the following phenomena can take place during aging and contribute to the hardening of the alloy: β decomposition into fine secondary α laths; transformation of the metastable martensitic α′ into the equilibrium α phase; and precipitation of the intermetallic Ti3Al. The composition and distribution of the β phase was shown to affect the precipitation of secondary α during aging, while the composition of the α phase plays a key role on the formation of Ti3Al. In situ X-ray diffraction studies of the early stages of aging show the kinetics of the α′ → α conversion by the reduction in FWHM of XRD reflections, indicate the contribution to hardening by the increase of the c/a ratio and the consequent limitation of active slip systems and depict the chemical homogenization and decomposition of the β phase.},
note = {Online available at: \url{https://doi.org/10.1016/j.matchar.2020.110400} (DOI). Callegari, B.; Oliveira, J.; Aristizabal, K.; Coelho, R.; Brito, P.; Wu, L.; Schell, N.; Soldera, F.; Mücklich, F.; Pinto, H.: In-situ synchrotron radiation study of the aging response of Ti-6Al-4V alloy with different starting microstructures. Materials Characterization. 2020. vol. 165, 110400. DOI: 10.1016/j.matchar.2020.110400}}