@misc{wang_microstructure_and_2020, author={Wang, K., Wang, J., Dou, X., Huang, Y., Hort, N., Gavras, S., Liu, S., Cai, Y., Pan, F.}, title={Microstructure and mechanical properties of large-scale Mg-Gd-Y-Zn-Mn alloys prepared through semi-continuous casting}, year={2020}, howpublished = {journal article}, doi = {https://doi.org/10.1016/j.jmst.2020.04.013}, abstract = {Large-scale Mg-8Gd-4Y-1Zn-Mn (wt.%) alloy ingot with a diameter of 315 mm and a length of 2410 mm was prepared through semi-continuous casting. Chemical composition, microstructure and mechanical properties at different locations of the samples with as-cast, T4 and T6 heat-treated states, respectively, were investigated. No obvious macro segregation has been detected in the high-quality alloy ingot. The main eutectic structures at all different locations are composed of α-Mg, Mg3RE-type, Mg5RE-type and LPSO phases. At the edge of ingot, the unusual casting twins including extension twins and compression twins were observed due to the intensive internal stress. In T4 heat-treated alloy, the micro segregation was eliminated. The remained phases were α-Mg and LPSO phase. Combined with the remarkable age-hardening response, T6 samples exhibits improved mechanical properties at ambient temperature, which derives from the dense prismatic β' precipitates and profuse basal γ' precipitates.}, note = {Online available at: \url{https://doi.org/10.1016/j.jmst.2020.04.013} (DOI). Wang, K.; Wang, J.; Dou, X.; Huang, Y.; Hort, N.; Gavras, S.; Liu, S.; Cai, Y.; Pan, F.: Microstructure and mechanical properties of large-scale Mg-Gd-Y-Zn-Mn alloys prepared through semi-continuous casting. Journal of Materials Science and Technology. 2020. vol. 52, 72-82. DOI: 10.1016/j.jmst.2020.04.013}}