@misc{cipriano_fundamentals_of_2018, author={Cipriano, G.P., Blaga, L.A., dos Santos, J.F., Vilaca, P., Amancio-Filho, S.T.}, title={Fundamentals of Force-Controlled Friction Riveting: Part I - Joint Formation and Heat Development}, year={2018}, howpublished = {journal article}, doi = {https://doi.org/10.3390/ma11112294}, abstract = {This work presents a systematic study on the correlations between process parameters and rivet plastic deformation, produced by force-controlled friction riveting. The 5 mm diameter AA2024 rivets were joined to 13 mm, nominal thickness, polyetherimide plates. A wide range of joint formations was obtained, reflecting the variation in total energy input (24–208 J) and process temperature (319–501 °C). The influence of the process parameters on joint formation was determined, using a central composite design and response surface methodology. Friction time displayed the highest contribution on both rivet penetration (61.9%) and anchoring depth (34.7%), and friction force on the maximum width of the deformed rivet tip (46.5%). Quadratic effects and two-way interactions were significant on rivet anchoring depth (29.8 and 20.8%, respectively). Bell-shaped rivet plastic deformation—high mechanical interlocking—results from moderate energy inputs (~100 J). These geometries are characterized by: rivet penetration depth of 7 to 9 mm; maximum width of the deformed rivet tip of 9 to 12 mm; and anchoring depth higher than 6 mm. This knowledge allows the production of optimized friction-riveted connections and a deeper understanding of the joining mechanisms, further discussed in Part II of this work.}, note = {Online available at: \url{https://doi.org/10.3390/ma11112294} (DOI). Cipriano, G.; Blaga, L.; dos Santos, J.; Vilaca, P.; Amancio-Filho, S.: Fundamentals of Force-Controlled Friction Riveting: Part I - Joint Formation and Heat Development. Materials. 2018. vol. 11, no. 11, 2294. DOI: 10.3390/ma11112294}}