%A Gan, W.M., Zheng, M.Y., Chang, H., Wang, X.J., Qiao, X.G., Wu, K., Schwebke, B., Brokmeier, H.-G.

%D 2009
%J Journal of Alloys and Compounds
%N 1-2
%P 256-262 
%R doi:10.1016/j.jallcom.2008.02.030
%T Microstructure and tensile property of the ECAPed pure magnesium
%U https://doi.org/10.1016/j.jallcom.2008.02.030
1-2 
%X the following ECAP. Due to a relatively high processing temperature, the refinement degree was limited via these three routes processing. Different preferred orientations of the basal plane were formed with three routes processing and there existed a rotation angle in (0002) pole figure fromnormal direction to transverse direction.Negative slope of the yield stress versus d−1/2 was obtained with routes Bc processing, which was attributed to the texture modification. Texture strengthening greatly increased the 0.2% yield strength, but decreased the ductility.