title={Texture Formation of Alpha2-Ti3Al during Hot Forming of Gamma-TiAl Based Alloys},
year={2011},
howpublished = {journal article},
doi = {https://doi.org/10.1557/opl.2011.32},
abstract = {Depending on the deformation temperature the γ-TiAl deformation texture consists of pure deformation components (700 °C) or components completely related to dynamic recrystallization (1100 °C). In contrast to the γ phase the α2 phase shows no remarkable changing of the deformation texture with increasing temperature. The α2 deformation texture basically consists of a similar component as it is known from hexagonal α-Ti, namely a tilted basal fiber. However, a significant influence of the deformation rate on the α2 texture formation is observed at temperatures above 800 °C. With increasing deformation temperature the α2 texture strengthens by applying a high deformation rate, whereas it weakens for a low deformation rate. This contrary behavior is attributed to the interaction of the α2 and γ phases during texture formation.},
note = {Online available at: \url{https://doi.org/10.1557/opl.2011.32} (DOI). Stark, A.; Gosslar, D.; Pashkov, N.: Texture Formation of Alpha2-Ti3Al during Hot Forming of Gamma-TiAl Based Alloys. MRS Online Proceedings Library. 2011. vol. 1295, 189-194. DOI: 10.1557/opl.2011.32}}