@misc{srinivasan_a_study_2009, 
author={Srinivasan, P.B., Zettler, R., Blawert, C., Dietzel, W.},
title={A study on the effect of plasma electrolytic oxidation on the stress corrosion cracking behaviour of a wrought AZ61 magnesium alloy and its friction stir weldment},
year={2009},
howpublished = {journal article},
doi = {https://doi.org/10.1016/j.matchar.2008.10.010},
abstract = {behaviour. The effect of surface modification in the form of a plasma electrolytic oxidation (PEO) coating on the corrosion behaviour of the weldment was assessed. The weldment exhibited a joint efficiency of 94%, nevertheless, the weld nugget region was found to have a higher susceptibility to SCC than its parent material counterpart. Even though the PEO coating had provided a good resistance to general and pitting corrosion, it could not completely prevent SCC of this weldment in ASTM D1384 solution.},
note = {Online available at: \url{https://doi.org/10.1016/j.matchar.2008.10.010} (DOI). Srinivasan, P.; Zettler, R.; Blawert, C.; Dietzel, W.: A study on the effect of plasma electrolytic oxidation on the stress corrosion cracking behaviour of a wrought AZ61 magnesium alloy and its friction stir weldment. Materials Characterization. 2009. vol. 60, no. 5, 389-396. DOI: 10.1016/j.matchar.2008.10.010}}