%A Bergner, F., Ulbricht, A., Hernandez-Mayoral, M., Pranzas, P.K.

%D 2008
%J Journal of Nuclear Materials
%N 1-2
%P 334-337 
%R doi:10.1016/j.jnucmat.2007.07.008
%T Small-angle neutron scattering study of neutron-irradiated iron and an iron–nickel alloy
%U https://doi.org/10.1016/j.jnucmat.2007.07.008
1-2 
%X The nature of irradiation-induced features in Fe–3wt%Ni was investigated by means of small-angle neutron scattering and hardness measurements and compared with results for commercially pure Fe. We have observed a three times larger volume fraction of irradiation-induced scatterers for the Fe–Ni alloy than for pure Fe. A vacancy–Ni ratio of 0.4–0.5 was deduced for the average scatterer. This finding is consistent with the hardness increase observed.