%0 journal article
%@ 1996-1944
%A Kurz, G.,Ganne, K.,Nienaber, M.,Bohlen, J.

%D 2023
%J Materials
%N 12
%P 4227 
%R doi:10.3390/ma16124227
%T Microstructure and texture evolution of the magnesium alloy ZMX210 during rolling and annealing
%U https://doi.org/10.3390/ma16124227
12 
%X The processability during massive deformation of magnesium-wrought products is hampered by the low formability of magnesium alloys. The research results of recent years demonstrate that rare earth elements as alloying elements improve the properties of magnesium sheets, such as formability, strength and corrosion resistance. The substitution of rare earth elements by Ca in Mg-Zn-based alloys results in a similar texture evolution and mechanical behaviour as RE-containing alloys. This work is an approach to understanding the influence of Mn as an alloying element to increase the strength of a Mg-Zn-Ca alloy. For this aim, a Mg-Zn-Mn-Ca alloy is used to investigate how Mn affects the process parameters during rolling and the subsequent heat treatment. The microstructure, texture and mechanical properties of rolled sheets and heat treatment at different temperatures are compared. The outcome of casting and the thermo-mechanical treatment are used to discuss how to adapt the mechanical properties of magnesium alloy ZMX210. The alloy ZMX210 behaves very similarly to the ternary Mg-Zn-Ca alloys. The influence of the process parameter rolling temperature on the properties of the ZMX210 sheets was investigated. The rolling experiments show that the ZMX210 alloy has a relatively narrow process window.