%A Froend, M.,Bock, F.,Ventzke, V.,Riekehr, S.,Kashaev, N.,Klusemann, B.,Enz, J.

%D 2018
%J Materials Science Forum, THERMEC 2018
%N 
%P 988-994 
%R doi:10.4028/www.scientific.net/MSF.941.988
%T Experimental Investigation of Temperature Distribution during Wire-Based Laser Metal Deposition of the Al-Mg Alloy 5087
%U https://doi.org/10.4028/www.scientific.net/MSF.941.988
 
%X Wire-based laser metal deposition enables to manufacture large-scale components with deposition rates significant higher compared to powder-based laser additive manufacturing techniques, which are currently working with deposition rates of only a few hundred gram per hour. However, the wire-based approach requires a significant amount of laser power in the range of several kilowatts instead of only a few hundred watts for powder-based processes. This excessive heat input during laser metal deposition can lead to process instabilities such as a non-uniform material deposition and to a limited processability, respectively. Although, numerous possibilities to monitor temperature evolution during processing exist, there is still a lack of knowledge regarding the relationship between temperature and geometric shape of the deposited structure. Due to changing cooling conditions with increasing distance to the substrate material, producing a wall-like structure results in varying heights of the individual tracks. This presents challenges for the deposition of high wall-like structures and limits the use of constant process parameters. In the present study, the temperature evolution during laser metal deposition of AA5087 using constant process parameters is investigated and a scheme for process parameter adaptions in order to reduce residual stress induced componential distortions is suggested.