%0 journal article
%@ 0966-9795
%A Schwaighofer, E.,Rashkova, B.,Clemens, H.,Stark, A.,Mayer, S.

%D 2014
%J Intermetallics
%N 
%P 173-184 
%R doi:10.1016/j.intermet.2013.11.011
%T Effect of carbon addition on solidification behavior, phase evolution and creep properties of an intermetallic Beta-stabilized Gamma-TiAl based alloy
%U https://doi.org/10.1016/j.intermet.2013.11.011
 
%X Improving mechanical properties of advanced intermetallic multi-phase γ-TiAl based alloys, such as the Ti-43.5Al-4Nb-1Mo-0.1B alloy (in at.%), termed TNM alloy, is limited by compositional and microstructural adaptations. A common possibility to further improve strength and creep behavior of such β-solidifying TiAl alloys is e.g. alloying with β-stabilizing substitutional solid solution hardening elements Nb, Mo, Ta, W as well as the addition of interstitial hardening elements C and N which are also carbide and nitride forming elements. Carbon is known to be a strong α-stabilizer and, therefore, alloying with C is accompanied by a change of phase evolution. The preservation of the solidification pathway via the β-phase, which is needed to obtain grain refinement, minimum segregation and an almost texture-free solidification microstructure, in combination with an enhanced content of C, requires a certain amount of β-stabilizing elements, e.g. Mo. In the present study, the solidification pathway, C-solubility and phase evolution of C-containing TNM variants are investigated. Finally, the creep behavior of a refined TNM alloy with 1.5 at.% Mo and 0.5 at.% C is compared with that exhibiting a nominal Ti-43.5Al-4Nb-1Mo-0.1B alloy composition.