%T Shear Localization in Gamma-Based Titanium Aluminides
%U 
1 
%X Hot-working of intermetallic γ titanium aluminides is often hampered by their liability to shear localization and subsequent crack formation, thereby preventing a refinement of the microstructure by dynamic recrystallization. The mechanisms leading to shear localization and cracking were microstructurally analyzed using scanning (SEM) and transmission (TEM) electron microscopic techniques.