%A Carmele, D.,Meyer, S.,Rieger, T.,Herrmann, K.,Lippmann, T.,Stark, A.,Bleck, W.,Klemradt, U.

%D 2012
%J Advanced Materials Research, THERMEC 2011
%N 
%P 660-665 
%R doi:10.4028/www.scientific.net/AMR.409.660
%T Very hard synchrotron x-ray radiation as an advanced characterization method exemplarily applied to advanced high-strength steels
%U https://doi.org/10.4028/www.scientific.net/AMR.409.660
 
%X Innovative steel materials of the third generation of advanced high-strength steel (AHSS) are based on complex multiphase microstructures on a submicron scale, which are adjusted in a heat treatment procedure. Established methods for microstructural characterization are usually applied after the heat treatment process (ex-situ) at room temperature and comprise amongst others X-ray analysis based on laboratory tubes with photon energies of several keV. The corresponding penetration depths are on the micron scale. Additionally, the results may be affected by the metallographic preparation process. Using very hard synchrotron X-ray radiation with photon energies of up to 100 keV, penetration depths in the millimetre range are realized and macroscopic volumes (mm³) can be investigated. Furthermore the photon flux of synchrotron sources is several orders of magnitude higher compared to laboratory tubes. Consequently in-situ measurements during a heat treatment process can be performed. Using the example of the standardized multiphase TRIP steel HCT690T, a microstructural investigation with high energy synchrotron X-ray radiation is discussed and compared to established diffraction methods using Co-and Cu-Kα-radiation. In-situ diffraction measurements during a heat treatment are exemplarily shown.