%T The interfacial diffusion zone in magnetron sputtered Ni-Ti thin films deposited on different Si substrates studied by HR-TEM
%U https://doi.org/10.4028/www.scientific.net/MSF.587-588.820
 
%X Ni-Ti Shape Memory Alloy thin films are suitable materials for microelectromechanical devices. During the deposition of Ni-Ti thin films on Si substrates, there exist interfacial diffusion and chemical interactions at the interface due to the high temperature processing necessary to crystallize the film. For the present study, Ni-Ti thin films were prepared by magnetron cosputtering from Ni-Ti and Ti targets in a specially designed chamber mounted on the 6-circle,goniometer of the ROssendorf BeamLine (ROBL-CRG) at ESRF, Grenoble (France). The objective,of this study has been to investigate the interfacial structure resulting from depositions (at a temperature of ≈ 470°C) on different substrates: naturally oxidized Si(100), Si(111) and poly-Si substrates. A detailed High-Resolution TEM analysis of the interfacial structure has been performed. When Ni-Ti is deposited on Si(100) substrate, a considerable diffusion of Ni into the substrate takes place, resulting in the growth of semi-octaeder A-NiSi2 silicide. In the case of Ni-Ti deposited on Si(111), there appears an uniform thickness plate, due to the alignment between substrate orientation and the [111]-growth front. For Ni-Ti deposited on poly-Si, the diffusion is,inhomogeneous. Preferential diffusion is found along the columnar grains of poly-Si, which are favourably aligned for Ni diffusion. These results show that for the Ni-Ti/Si system, the morphology,of the diffusion interface is strongly dependent on the type of substrates.