%0 journal article
%@ 1359-6462
%A Kannan, M.B.,Dietzel, W.,Singh Raman, P.K.,Lyon, P.
%D 2007
%J Scripta Materialia
%N 7
%P 579-581 
%R doi:10.1016/j.scriptamat.2007.06.019
%T Hydrogen-induced-cracking in magnesium alloy under cathodic polarisation
%U https://doi.org/10.1016/j.scriptamat.2007.06.019
7 
%X The hydrogen-induced-cracking (HIC) behaviour of the magnesium alloy AZ80 was evaluated using the slow strain rate testmethod. The study shows no evidence of HIC in AZ80 alloy after pre-exposure and pre-charging conditions in distilled water. However, under continuous charging in distilled water during straining, the AZ80 alloy shows evidence of HIC. The contradiction,reported in the literature is addressed.