%0 journal article
%@ 0947-5117
%A Strehl, G.,Beaven, P.,Lesage, B.,Borchardt, G.

%D 2005
%J Materials and Corrosion
%N 11
%P 778-784 
%R doi:10.1002/maco.200503878
%T Two calculations concerning the critical aluminium content in Fe20Cr5Al alloys
%U https://doi.org/10.1002/maco.200503878
11 
%X Alloys for high temperature applications rely on a protective,oxide layer formed by selective oxidation. In Fe20Cr5Al type alloys the useful lifetime is governed by the depletion of aluminium by oxidation down to a critical aluminium content. Following spallation of the oxide scale the bare metal is exposed to air and catastrophic failure due to breakaway oxidation occurs if the aluminium content is too low. In this paper a model for the calculation of the critical aluminium content is presented. Based on Wagner’s ideas on selective oxidation in ternary alloys, the critical aluminium content is calculated as that corresponding to the transition between external and internal oxidation. The resulting aluminium contents are temperature dependent and cover the range of values 0 to 3.5 wt.% reported in the literature.