title={The influence of heat treatment processing on microstructure and mechanical properties of Ti–24Nb–4Zr–8Sn alloy by powder metallurgy},
year={2020},
howpublished = {journal article},
doi = {https://doi.org/10.1016/j.mtla.2020.100803},
abstract = {Different heat treatments, including quenching and hot isostatic pressing, were conducted on the Ti–24Nb–4Zr–8Sn alloy fabricated by powder metallurgy, in order to improve its mechanical properties. As-sintered samples have high oxygen content over 3000 ppm, resulting in α phase precipitates and low ductility. But the mechanical properties can be improved by solution treatment at a suitable temperature and subsequent quenching. Although the treatment is only effective within a narrow temperature window ranging from 950 to 1000 °C, the treatment can completely eliminate the detrimental α phase and substantially improve the ductility of the alloy from 2% to 19.33%. In comparison, although the hot isostatic pressing can improve the density of the as-sintered alloy to nearly fully dense, it proves unable to remove the α phase from the material or improve its ductility alone.},
note = {Online available at: \url{https://doi.org/10.1016/j.mtla.2020.100803} (DOI). Li, X.; Zhou, Y.; Ebel, T.; Liu, X.; Shen, X.; Yu, P.: The influence of heat treatment processing on microstructure and mechanical properties of Ti–24Nb–4Zr–8Sn alloy by powder metallurgy. Materialia. 2020. vol. 13, 100803. DOI: 10.1016/j.mtla.2020.100803}}