@misc{dharmendra_deformation_microstructures_2012, 
author={Dharmendra, C.,Rao, K.P.,Prasad, Y.V.R.K.,Hort, N.,Kainer, K.U.},
title={Deformation Microstructures and Textures of Cast Mg-3Sn-2Ca Alloy under Uniaxial Hot Compression},
year={2012},
howpublished = {journal article},
doi = {https://doi.org/10.4028/www.scientific.net/AMM.152-154.322},
abstract = {The influence of deformation conditions on the microstructure and texture evolution during hot compression of Mg-3Sn-2Ca (TX32) has been studied. Cylindrical samples were compressed uniaxially at different combinations of temperatures and strain rates in the ranges 300-500 oC and 0.0003-10 s-1. The crystallographic orientation information of the as-cast and deformed specimens was obtained by EBSD micro-texture analysis. Activation of different slip systems was investigated using Schmid factor analysis and the results reinforce the importance of non-basal slip,for deformation at high temperatures. Samples deformed at 500 oC/0.1 s-1 resulted in a fully,recrystallized microstructure with near random crystallographic texture.},
note = {Online available at: \url{https://doi.org/10.4028/www.scientific.net/AMM.152-154.322} (DOI). Dharmendra, C.; Rao, K.; Prasad, Y.; Hort, N.; Kainer, K.: Deformation Microstructures and Textures of Cast Mg-3Sn-2Ca Alloy under Uniaxial Hot Compression. Applied Mechanics and Materials, Mechanical Engineering and Materials. 2012. vol. 152-154, 322-325. DOI: 10.4028/www.scientific.net/AMM.152-154.322}}