@misc{rao_high_temperature_2010, 
author={Rao, K.P.,Prasad, Y.V.R.K.,Hort, N.,Kainer, K.U.},
title={High Temperature Deformation Mechanisms and Processing Map for Hot Working of Cast-Homogenized Mg-3Sn-2Ca Alloy},
year={2010},
howpublished = {journal article},
doi = {https://doi.org/10.4028/www.scientific.net/MSF.638-642.3616},
abstract = {The hot working behavior of Mg-3Sn-2Ca alloy has been investigated in the temperature range 300–500 oC and strain rate range 0.0003–10 s-1, with a view to evaluate the mechanisms and optimum parameters of hot working. For this purpose, a processing map has been developed on the basis of the flow stress data obtained from compression tests. The stress-strain curves exhibited steady state behavior at strain rates lower than 0.01 s-1 and at temperatures higher than 350 oC and flow softening occurred at higher strain rates. The processing map exhibited two dynamic,recrystallization domains in the temperature and strain rate ranges: (1) 300–420 oC and 0.0003–,0.003 s-1, and (2) 420–500 oC and 0.003–1.0 s-1, the latter one being useful for commercial hot,working. Kinetic analysis yielded apparent activation energy values of 161 and 175 kJ/mole in,domains (1) and (2) respectively. These values are higher than that for self-diffusion in magnesium,suggesting that the large volume fraction of intermetallic particles CaMgSn present in the matrix,generates considerable back stress. The processing map reveals a wide regime of flow instability,which gets reduced with increase in temperature or decrease in strain rate.},
note = {Online available at: \url{https://doi.org/10.4028/www.scientific.net/MSF.638-642.3616} (DOI). Rao, K.; Prasad, Y.; Hort, N.; Kainer, K.: High Temperature Deformation Mechanisms and Processing Map for Hot Working of Cast-Homogenized Mg-3Sn-2Ca Alloy. Materials Science Forum, THERMEC 2009. 2010. vol. 638-642, 3616-3621. DOI: 10.4028/www.scientific.net/MSF.638-642.3616}}