@misc{kannan_hydrogeninducedcracking_in_2007, 
author={Kannan, M.B.,Dietzel, W.,Singh Raman, P.K.,Lyon, P.},
title={Hydrogen-induced-cracking in magnesium alloy under cathodic polarisation},
year={2007},
howpublished = {journal article},
doi = {https://doi.org/10.1016/j.scriptamat.2007.06.019},
abstract = {The hydrogen-induced-cracking (HIC) behaviour of the magnesium alloy AZ80 was evaluated using the slow strain rate testmethod. The study shows no evidence of HIC in AZ80 alloy after pre-exposure and pre-charging conditions in distilled water. However, under continuous charging in distilled water during straining, the AZ80 alloy shows evidence of HIC. The contradiction,reported in the literature is addressed.},
note = {Online available at: \url{https://doi.org/10.1016/j.scriptamat.2007.06.019} (DOI). Kannan, M.; Dietzel, W.; Singh Raman, P.; Lyon, P.: Hydrogen-induced-cracking in magnesium alloy under cathodic polarisation. Scripta Materialia. 2007. vol. 57, no. 7, 579-581. DOI: 10.1016/j.scriptamat.2007.06.019}}