@misc{zander_the_catalytic_2006, 
author={Zander, D.,Lyubenova, L.,Koester, U.,Dornheim, M.,Aguey-Zinsou, F.,Klassen, T.},
title={The catalytic effect of Nb2O5 on the electrochemical hydrogenation of nanocrystalline magnesium},
year={2006},
howpublished = {journal article},
doi = {https://doi.org/10.1016/j.jallcom.2005.06.063},
abstract = {Nanocrystalline Mg powder without and with 2 mol% Nb2O5 catalyst was studied in a 6M KOH electrolyte as electrode material for electrochemical hydrogen charging processes. Since the hydrogen overpotential of Mg, which is a measure of the hydrogen evolution at the electrode surface, was observed to be reduced by the addition of Nb2O5, it is assumed that the catalyst influences the electrode reactions.,Considering this assumption hydrogenation was studied at different current densities. The storage capacity as well as the kinetic of Mg/Nb2O5 electrodes increased significantly up to 1 wt.% H2 at a charging time of 30 min with decreasing current density. The storage capacity of nanocrystalline Mg powder showed only minor changes to lower hydrogen contents with decreasing current density.},
note = {Online available at: \url{https://doi.org/10.1016/j.jallcom.2005.06.063} (DOI). Zander, D.; Lyubenova, L.; Koester, U.; Dornheim, M.; Aguey-Zinsou, F.; Klassen, T.: The catalytic effect of Nb2O5 on the electrochemical hydrogenation of nanocrystalline magnesium. Journal of Alloys and Compounds. 2006. vol. 413, no. 1-2, 298-301. DOI: 10.1016/j.jallcom.2005.06.063}}